Product Details
DESCRIPTION
BorPure™MB6561 is a multimodal, high-density polyethylene intended for both injection and compression moulding. This grade exhibits excellent organoleptic properties and very good flow properties with good impact strength.
The broad molecular weight distribution guarantees superior environmental stress crack resistance
CAS-No. 25087-34-7
APPLICATIONS
- Caps and closures for taste-sensitive beverages like water.
- Consumer and industrial articles with high ESCR demands
KEY FEATURES
- Excellent organoleptic properties.
- Superior Environmental stress crack resistance
- Easy and versatile processability.
- Good impact strength.
PROCESSING CONDITIONS
This product is easy to process with standard injection moulding machines, as well as on compression moulding equipment
Injection Moulding
Following injection moulding parameters should be used as guidelines:
- Melt temperature: 190 - 250 °C
- Mould temperature: 10 - 40 °C
- Injection speed: As high as possible.
Shrinkage 1 - 2 %, depending on wall thickness and moulding parameters
Compression Moulding
Following compression moulding parameters should be used as guidelines
- Extruder temperature profile 160 - 195 °C
- Melt temperature: 180 - 200 °C
- Mould temperature: 10 - 40 °C
Shrinkage 1 - 2 %, depending on wall thickness and moulding parameters
Please contact your local Borouge representative for specific recommendations for processing conditions
PHYSICAL PROPERTIES
| Property Typical Value* Test Method | ||
| Density | 955 kg/m³ | ISO 1183 |
| Melt Flow Rate (190°C/2.16kg) | 1.5 g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 920 MPa | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 24.0 MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 0.095 | ISO 527-2 |
| Tensile Stress at Break (50mm/min) | 14 MPa | ISO 527-2 |
| Tensile Strain at Break (50mm/min) | 4 | ISO 527-2 |
| Flexural modulus (2mm/min) | 980 MPa | ISO 178 |
| Charpy Notched Strength (23°C, 1eA, Edgewise) | 14.0 kJ/m² | ISO 179-1 |
| Shore Hardness (Shore D, 15 sec.) | 60 | ISO 868 |
| Shore Hardness (Shore D, 1 sec.) | 63.5 | ASTM D2240 |
| VICAT Softening Temperature (A50) | 125°C | ISO306 |
| VICAT Softening Temperature (B50) | 70°C | ISO306 |
| Temperature of deflection under load (DTUL) | 64°C | ISO 75-2 |
| ESCR (10% Igepal – F50) | 400 Hours | ASTM D1693-B |
| FNCT (2% Arkopal, 6.0Mpa, 50°C) | 40 Hours | ISO 16770 |